Description
PRODUCT FEATURES
- Excellent weather resistance, aging resistance, tensile strength and elongation.
- Operation can be done on wet substrate. Directly expose to the weather
- Repeat welding is possible.
- White color TPO to increase reflection of sun rays
- Ability of resist the growth of mould and alga
SPECIFICATION
|
Product name
|
Nominal length
|
Nominal width
|
Thickness
|
|---|---|---|---|
|
Aquaprufe TPO waterproof membrane
|
20m
|
2.0m
|
1.2mm, 1.5mm,
|
|
1.8mm, 2.0mm
|
DATABASE
| Item | Index | |||
|---|---|---|---|---|
| H | L | P | ||
|
Thickness above scrim
|
–
|
0.40
|
||
|
Tensile performance
|
Max.Tensile strength,(N/cm)≥
|
–
|
200
|
250
|
|
Tensile Strength, Mpa≥
|
12
|
–
|
–
|
|
|
Elongation at max. tensile strength.% ≥
|
–
|
–
|
15
|
|
|
Elongation at break,% ≥
|
500
|
250
|
–
|
|
|
Dimensional change after heat treatment
|
2.0
|
1.0
|
0.5
|
|
|
Flexibility at low temperature
|
-40℃, no cracking
|
|||
|
Water tightness
|
0.3MPa, 2h, water tight
|
|||
|
Puncture Resistance
|
0.5kg?m, impermeable
|
|||
|
Hydrostatic Resistance
|
–
|
20kg, impermeable
|
||
|
Lap seam peeling strength
|
4.0 or membranebreakage
|
3.0
|
||
|
Right-angled tear strength
|
60
|
–
|
–
|
|
|
Trapezoid tear strength
|
–
|
250
|
450
|
|
|
Water absorption
|
After immersion ≤
|
4.0
|
||
|
After drying ≤
|
-4.0
|
|||
|
Heat aging
|
Period,h
|
672
|
||
|
Appearance
|
No bubbling,crack,layered, bonding nor hole
|
|||
|
Retention rate at max. Tension,% ≥
|
90
|
|||
|
Elongation retention rate at max tension,% ≥
|
90
|
|||
|
Flexibility at low temperature
|
-40℃, no cracking
|
|||
|
Chemical resistance
|
Appearance
|
No bubbling,crack,layered, bonding nor hole
|
||
|
Retention rate at max. Tension,% ≥
|
90
|
|||
|
Elongation retention rate at max tension,% ≥
|
90
|
|||
|
Flexibility at low temperature
|
-40℃, no cracking
|
|||
|
Artificial weathering aging
|
Period,h
|
1500
|
||
|
Appearance
|
No bubbling,crack,layered, bonding nor hole
|
|||
|
Retention rate at max. Tension,% ≥
|
90
|
|||
|
Elongation retention rate at max tension,% ≥
|
90
|
|||
|
Flexibility at low temperature
|
-40℃, no cracking
|
|||
| A. The hydrostatic resistance is only applicable for the pressed roofing.
B. The period for the artificial weather aging test is 2500 h for the single ply roofing system. |
||||